Microstructure and Mechanical Properties of AA6061/AA5052/AA1050 Alloy Fabricated by Cold Roll-Bonding and Subsequently Annealed
(주)코리아스칼라
- 최초 등록일
- 2023.12.18
- 최종 저작일
- 2023.11
- 8페이지/
어도비 PDF
- 가격 4,000원
![할인쿠폰받기](/images/v4/document/ico_det_coupon.gif)
* 본 문서는 배포용으로 복사 및 편집이 불가합니다.
서지정보
ㆍ발행기관 : 한국재료학회
ㆍ수록지정보 : 한국재료학회지 / 33권 / 11호
ㆍ저자명 : Seong-Hee Lee, Sang-Hyeon Jo, Jae-Yeol Jeon
목차
1. Introduction
2. Experimental Procedure
3. Results and Discussion
4. Conclusions
Acknowledgement
영어 초록
Changes in the microstructure and mechanical properties of as-roll-bonded AA6061/AA5052/AA1050 threelayered sheet with increasing annealing temperature were investigated in detail. The commercial AA6061, AA5052 and AA1050 sheets with 2 mm thickness were roll-bonded by multi-pass rolling at ambient temperature. The roll-bonded Al sheets were then annealed for 1 h at various temperatures from 200 to 400 °C. The specimens annealed up to 250 °C showed a typical deformation structure where the grains are elongated in the rolling direction in all regions. However, after annealing at 300 °C, while AA6061 and AA1050 regions still retained the deformation structure, but AA5052 region changed into complete recrystallization. For all the annealed materials, the fraction of high angle grain boundaries was lower than that of low angle grain boundaries. In addition, while the rolling texture of the {110}<112> and {123}<634> components strongly developed in the AA6061 and AA1050 regions, in the AA5052 region the recrystallization texture of the {100}<001> component developed. After annealing at 350 °C the recrystallization texture developed in all regions. The as-rolled material exhibited a relatively high tensile strength of 282 MPa and elongation of 18 %. However, the tensile strength decreased and the elongation increased gradually with the increase in annealing temperature. The changes in mechanical properties with increasing annealing temperature were compared with those of other three-layered Al sheets fabricated in previous studies.