Measuring electrical resistances of ACF sensors by CO2 adsorption in a small chamber
* 본 문서는 배포용으로 복사 및 편집이 불가합니다.
서지정보
ㆍ발행기관 : 한국탄소학회
ㆍ수록지정보 : Carbon letters / 32권 / 1호
ㆍ저자명 : Dae Wan Kim, Lee Ku Kwac, Hong Gun Kim, Seung Kon Ryu
ㆍ저자명 : Dae Wan Kim, Lee Ku Kwac, Hong Gun Kim, Seung Kon Ryu
목차
Abstract1 Introduction
2 Experimental
2.1 Experimental materials
2.2 Experimental methods
3 Results and discussion
3.1 Characteristics of ACF
3.2 Electrical resistance according to temperature and humidity
3.3 CO2 adsorption characteristics of ACF
4 Conclusions
References
영어 초록
The electrical resistances of small-sized activated carbon fiber (ACF) fabric (specific surface area: 1244.7 m2/ g, average pore diameter: 1.92 nm) and felt (specific surface area: 1321.2 m2/ g, average pore diameter: 2.21 nm) sensors were measured in a temperature and humidity controlled gas chamber by CO2 adsorption at different surrounding CO2 concentrations (3000–10,000 ppm). The electrical resistances of ACF sensors decreased linearly as the increase of temperature and decreased exponentially as the increase of humidity in the ambient atmospheric chamber. The electrical resistances of ACF rapidly decreased within 4 s and an equilibrium state was achieved within 10 s due to the very rapid CO2 adsorption at room temperature and 40% humidity. Comparing the difference in electrical resistance values measured during injection of similar concentrations of CO2 after reaching the equilibrium value, the fabric exhibited a significant change, whereas the felt did not, even though it had a relatively larger specific surface area. The reason is that micropore volume greatly affected the amount of CO2 adsorbed, whereas the specific surface area did not affect it as much. Therefore, ACF fabric with large micropores (> 2.0 nm) can be developed and used as CO2 sensors in small rooms such as a passenger vehicles.참고 자료
없음"Carbon letters"의 다른 논문
Improving wettability and adhesion of carbon cloth with..9페이지
Carbon‑coated SiOx anode materials via PVD and pyrolyze..8페이지
Replacement effect of fresh electrolyte on the accelera..7페이지
Gamma‑ray irradiated graphene nanosheets/polydopamine h..8페이지
Mesoporous carbon microspheres fabricated from KOH acti..10페이지
Preparation and capacitive property of graphene oxide c..11페이지
Preparation of cathode slurry for lithium‑ion battery b..8페이지
Hierarchically porous carbon derived from tobacco waste..13페이지
Microporous‑activated carbons of type I adsorption isot..21페이지
Preparation and properties of Joule thermal effect self..12페이지