Microstructure and electrical properties of carbon short fiber reinforced copper composites fabricated by electroless deposition followed by powder metallurgy process
* 본 문서는 배포용으로 복사 및 편집이 불가합니다.
서지정보
ㆍ발행기관 : 한국탄소학회
ㆍ수록지정보 : Carbon letters / 30권 / 3호
ㆍ저자명 : Walid M. Daoush, Turki S. Alkhuraiji, Moath A. Khamis, Turki S. Albogmy
ㆍ저자명 : Walid M. Daoush, Turki S. Alkhuraiji, Moath A. Khamis, Turki S. Albogmy
목차
Abstract1 Introduction
2 Materials and methods
2.1 Starting materials
2.2 Methods
3 Results and discussion
3.1 Powder fabrication and characterization
3.2 DTA and TGA
3.3 Powder consolidation and characterizations
3.4 Density and porosity
3.5 Electrical resistivity and conductivity
4 Conclusion
Acknowledgements
References
영어 초록
Carbon short fibers/copper composites with different carbon short fiber contents up to 15 wt.% as reinforcements are prepared to investigate the influence of the carbon short fiber surface coating on the microstructure, density, and electrical properties of the carbon short fibers/copper composites. The carbon short fibers were surface treated by acid functionalization followed by alkaline treatment before the coating process. It was observed from the results that coated type copper nanoparticles were deposited on the surface of the carbon short fibers. The surface treated carbon short fibers were coated by copper using the electroless deposition technique in the alkaline tartrate bath by using formaldehyde as a reducing agent of the copper sulfate. The produced coated carbon short fibers/copper composite powders were cold compacted at 600 MPa, and then sintered at 875 °C for 2 h under (hydrogen/nitrogen 1:3) atmosphere. A reference copper sample was also prepared by the same method to compare between the properties of pure copper and the carbon short fibers/copper composites. The phase composition, morphology, and microstructure of the prepared carbon short fibers/copper composite powders as well as the corresponding carbon short fibers/copper composites were investigated using X-ray diffraction analysis (XRD) and scanning electron microscope (SEM) equipped with an energy-dispersive spectrometer (EDS), respectively. The density and the electrical resistivity of the sintered composites were measured. It was observed from the results that the density was decreased; however, the electrical resistivity was increased by increasing the carbon short fibers wt.%.참고 자료
없음태그
"Carbon letters"의 다른 논문
Influence of oxyfluorinated graphite on fluorinated eth..8페이지
Heteroatoms in situ‑doped hierarchical porous hollow‑ac..14페이지
A complementary analysis of the porous structure of bio..5페이지
Preparation and electrochemical properties of self‑dope..10페이지
Synthesis and characterization of activated carbon prod..7페이지
Facile preparation of activated carbon with optimal por..9페이지
Low thermal conductivity carbon material from electrosp..8페이지
Trichloroethylene adsorption from aqueous solutions by ..7페이지
Fracture mechanism characteristics of ultra‑thin choppe..10페이지
Structural characteristics and sodium penetration behav..11페이지