피복입자핵연료에서 증착조건이 탄화규소층의 특성에 미치는 영향

서지정보

ㆍ발행기관 : 한국분말야금학회 ㆍ수록지정보 : 한국분말야금학회지 / 23권 / 5호
ㆍ저자명 : 김연구, 김원주, 여승환, 조문성

목차

Abstract
1. 서 론
2. 실험방법
3. 결과 및 고찰
4. 결 론
References

영어 초록

Tri-isotropic (TRISO) coatings on zirconia surrogate beads are deposited using a fluidized-bed vapor deposition (FB-CVD) method. The silicon carbide layer is particularly important among the coated layers because it acts as a miniature pressure vessel and a diffusion barrier to gaseous and metallic fission products in the TRISO-coated particles. In this study, we obtain a nearly stoichiometric composition in the SiC layer coated at 1400oC, 1500oC, and 1400oC with 20 vol.% methyltrichlorosilane (MTS), However, the composition of the SiC layer coated at 1300-1350oC shows a difference from the stoichiometric ratio (1:1). The density decreases remarkably with decreasing SiC deposition temperature because of the nanosized pores. The high density of the SiC layer (≥ 3.19 g/cm2) easily obtained at 1500oC and 1400oC with 20 vol.% MTS did not change at an annealing temperature of 1900°C, simulating the reactor operating temperature. The evaluation of the mechanical properties is limited because of the inaccurate values of hardness and Young’s modulus measured by the nano-indentation method.

참고 자료

없음