수계 콜로이드 계에서 교류 전계에 의한 입자 배열 제어
* 본 문서는 배포용으로 복사 및 편집이 불가합니다.
서지정보
ㆍ발행기관 : 한국재료학회
ㆍ수록지정보 : 한국재료학회지 / 23권 / 1호
ㆍ저자명 : 황연
ㆍ저자명 : 황연
영어 초록
The alignments of polystyrene particles of 1μm and 5μm sizes in an aqueous colloidal system were observed by varying the electric field strength, the frequency and the water flow. Spherical mono-dispersed polystyrene particles dispersed in pure water were put into a perfusion chamber; an AC electric field was applied to the Au/Cr electrodes with a 4 mm gap on the glass substrate. The mixture of the 1μm and 5μm sized polystyrene particles at 0.5 vol% concentrations for each size was set in the dielectrophoresis conditions of 1 kHz and 150 V/cm. Large particles of 5μm size were aligned to form chains as the result of the dielectrophoresis force interaction. On the contrary, small particles of 1μm size did not form chains because the dielectrophoresis force was not sufficiently large. When the electric field increased to 250 V/cm, small particles were able to form chains. After the chains were formed from both large and small particles, they began to coalescence as time passed. Owing to the electroosmotic flow of water, wave patterns along the perpendicular direction of the applied electric field appeared at the conditions of 200 Hz and 50 V/cm, when the dielectrophoresis force was small. This wave pattern also appeared for small particles at 1 kHz and 150 V/cm conditions due to the flow of solvent when water was forced to circulate.참고 자료
없음"한국재료학회지"의 다른 논문
마그네슘합금의 표면처리에 관한 연구개발 동향9페이지
나노크기 Cu 분산입자를 갖는 Al2O3 다공체의 제조 및 미세조직 특성5페이지
Optical Properties of Opal Glass on the Various Content..8페이지
금 나노입자 형성을 이용한 계층구조 SiO2 코팅층의 제조 및 표면 특성6페이지
유도결합 플라즈마 화학기상증착법에 의해 활성화된 탄소원자를 이용한 Ni/SiO2/Si 기판에서 그래..6페이지
ARB공정에 따른 초미세립 AA1050/AA6061 복합알루미늄 합금 판재의 미세조직 발달6페이지
50 ㎛ 기판을 이용한 a-Si:H/c-Si 이종접합 태양전지 제조 및 특성 분석6페이지
Photoluminescence of Y3(Al, Ga)5O12:Ce3+ Nanoparticles ..4페이지
탄화온도 및 재담금 처리에 따른 중공형 탄소다공체의 기공구조 및 특성7페이지
극저온 열처리가 7075 알루미늄 합금의 잔류응력과 기계적 특성에 미치는 영향6페이지